Abstract

Mortar is a building material that functions as plastering, making paving blocks and others. The number of instant mortar products and products that are easily broken and cracked on the market, so it still needs to be strengthened. In this research, by adding nano-silica and coconut fibre. The purpose of this study was to determine the effect of adding nano-silica and coconut fibre to specific gravity, tensile strength and water absorption. This research method with experiments in the laboratory. Specimens of tensile strength and water absorption of cylinders with a size of 10 cm x 20 cm. The test results show that the tensile strength of instant mortar can be increased, while the results for the specific gravity of mortar meet the standard. Water absorption increases when added to coconut fibre.

Keywords: Mortar, Nano-Silica, Tensile Strength, Absorption.

Abstrak

Mortar adalah bahan bangunan yang berfungsi sebagai plesteran, membuat paving block dan lainnya. Banyaknya produksi dan produk mortar instan yang mudah pecah dan retak di pasaran, sehingga masih perlu diperkuat. Dalam penelitian ini, dengan menambahkan nano-silika dan serat kelapa. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh penambahan nano-silika dan serat kelapa pada berat jenis, kekuatan tarik dan penyerapan air. Metode penelitian ini dengan eksperimen di laboratorium. Spesimen kuat tarik dan daya serap air silinder dengan ukuran 10 cm x 20 cm. Hasil pengujian menunjukkan bahwa kekuatan tarik mortar instan dapat ditingkatkan, sedangkan hasil untuk berat jenis mortar memenuhi standar. Penyerapan air meningkat ketika ditambahkan dengan serat kelapa.

Kata kunci: Mortar, Nano-Silica, Kuat Tarik,  Penyerapan.